OEM Supply VFFS Packaging Film - Low Melting Point EVA Film – Zonpak
OEM Supply VFFS Packaging Film - Low Melting Point EVA Film – Zonpak Detail:
ZonpakTM low melting point EVA film is a special kind of packaging film which can be used on automatic form-fill-seal (FFS) bagging machines to make little bags of rubber additives (e.g. 100g-5000g). The bags of additives can be direct put into a mixer during rubber mixing process. Bags made of the film can easily melt and fully disperse into the rubber as an effective ingredient.
PROPERTIES:
- A wide range of melting points are available for different applications.
- With stable chemical properties, fits most rubber chemicals.
- With good physical strength, is suitable for most automatic bagging machines.
- Eliminate the disposal of packaging waste for the material users.
- Helps material users raise production efficiency while decrease material waste.
APPLICATIONS:
- peptizer, anti-aging agent, curing agent, aromatic hydrocarbon oil
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPa TD ≥16MPa |
| Elongation at break | MD ≥400% TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
Our firm sticks on the theory of "Quality will be the life in the enterprise, and status could be the soul of it" for OEM Supply VFFS Packaging Film - Low Melting Point EVA Film – Zonpak, The product will supply to all over the world, such as: Indonesia , Dominica , Wellington , Our tenet is "integrity first, quality best". We have confidence in providing you with excellent service and ideal products. We sincerely hope we can establish win-win business cooperation with you in the future!
By Julie
from Czech
- 2017.08.21 14:13
After the signing of the contract, we received satisfactory goods in a short term, this is a commendable manufacturer.
By Edward
from Hungary
- 2018.09.29 13:24