New Fashion Design for EVA Pouch – Low Melt EVA Pouches – Zonpak
New Fashion Design for EVA Pouch – Low Melt EVA Pouches – Zonpak Detail:
ZonpakTM low melt EVA pouches are made from EVA resin (Ethylene Vinyl Acetate), and are mainly used to pack rubber compounding ingredients (e.g. rubber process oil and other chemicals) in tire and rubber manufacture process. Due to the property of low melting point and good compatibility with rubber, the pouches together with the additives contained can be direct put into an internal mixer and fully disperse into the rubber as an effective ingredient, so it can provide accurate adding of additives and cleaner work environment. Using the pouches can help rubber plants get uniform rubber compounds, save additives and raise production efficiency.
Melting point, size and color can be customized according to the customers’ application requirement.
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPaTD ≥16MPa |
| Elongation at break | MD ≥400%TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPaTD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
We're going to commit ourselves to giving our esteemed buyers using the most enthusiastically considerate solutions for New Fashion Design for EVA Pouch – Low Melt EVA Pouches – Zonpak, The product will supply to all over the world, such as: Slovakia , Barcelona , The Swiss , We believe in establishing healthy customer relationships and positive interaction for business. Close cooperation with our customers has helped us to create strong supply chains and reap benefits. Our products have gained us widespread acceptance and the satisfaction of our worldwide valued clients.
By Cornelia
from Grenada
- 2017.08.18 18:38
We feel easy to cooperate with this company, the supplier is very responsible, thanks.There will be more in-depth cooperation.
By jari dedenroth
from Botswana
- 2017.11.20 15:58