High definition EVA Film Roll - Low Melting Point EVA Film – Zonpak
High definition EVA Film Roll - Low Melting Point EVA Film – Zonpak Detail:
ZonpakTM low melting point EVA film is a special kind of packaging film which can be used on a form-fill-seal (FFS) bagging machine to make little bags of rubber additives (e.g. 100g-5000g). The bags of additives can be direct put into an internal mixer during rubber mixing process. Bags made of the film can easily melt and fully disperse into the rubber as a minor ingredient.
PROPERTIES:
- A wide range of melting points are available for different applications.
- Stable chemical properties, fits most rubber chemicals.
- Good physical strength, suitable for most automatic bagging machines.
- Eliminate the disposal of packaging waste for the material users.
- Helps material users raise work efficiency while decrease waste of materials.
APPLICATIONS:
- peptizer, anti-aging agent, curing agent, aromatic hydrocarbon oil
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPa TD ≥16MPa |
| Elongation at break | MD ≥400% TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
No matter new customer or previous client, We believe in prolonged time period and trustworthy relationship for High definition EVA Film Roll - Low Melting Point EVA Film – Zonpak, The product will supply to all over the world, such as: Cambodia , Iraq , Jordan , Profession, Devoting are always fundamental to our mission. We've got always been in line with serving customers, creating value management objectives and adhering to the sincerity, dedication, persistent management idea.
By Miguel
from Panama
- 2018.09.29 17:23
Hope that the company could stick to the enterprise spirit of "Quality, Efficiency, Innovation and Integrity", it will be better and better in the future.
By Arthur
from Peru
- 2017.11.20 15:58