Best quality Low Melt EVA Film For FFS Packaging - EVA Film for Automatic FFS Packaging – Zonpak
Best quality Low Melt EVA Film For FFS Packaging - EVA Film for Automatic FFS Packaging – Zonpak Detail:
ZonpakTM EVA film is specially designed for automatic form-fill-seal (FFS) packaging of rubber chemicals. Manufacturers of rubber chemicals can use the film and FFS machines to make 100g-5000g uniform packages for rubber compounding or mixing plants. These little packages can be direct put into a mixer during the mixing process. The bag made of the film can easily melt and fully disperse into the rubber as an effective ingredient. It brings convenience to material users and helps raise production efficiency while decrease the cost and material waste.
Films with different melting points are available for different application. Thickness and width of the film can be custom made as customer required.
Technical Standards |
|
Melting point | 65-110 deg. C |
Physical properties | |
Tensile strength | MD ≥16MPaTD ≥16MPa |
Elongation at break | MD ≥400%TD ≥400% |
Modulus at 100% elongation | MD ≥6MPaTD ≥3MPa |
Appearance | |
Surface of the product is flat and smooth, there is no wrinkle, no bubble. |
Product detail pictures:
Related Product Guide:
Our group through specialist training. Skilled expert knowledge, sturdy sense of assistance, to fulfill the provider needs of shoppers for Best quality Low Melt EVA Film For FFS Packaging - EVA Film for Automatic FFS Packaging – Zonpak, The product will supply to all over the world, such as: Guinea , Mali , Tajikistan , we rely on own advantages to build a mutual-benefit commerce mechanism with our cooperative partners. As a result, now we have gained a global sales network reaching the Middle East, Turkey, Malaysia and Vietnamese.
By Esther from Cape Town - 2017.10.23 10:29
Wide range, good quality, reasonable prices and good service, advanced equipment, excellent talents and continuously strengthened technology forces,a nice business partner.
By Aurora from Portugal - 2018.09.23 17:37